Solid-State Ion och New Energy Technology för att lägga fram en slags teaminnovation, Thermal Expansion Compensation Strategy, implementerar bränslecellkatoden med andra batteri helt termiska mekaniska kompatibilitet mellan komponenter, för att lösa hinder för processen med Solid Oxide Fuel Cell (SOFC) kommersialisering av ett stort tekniskt svårt problem {{1)
Mechanical instability "hot" refers to a solid oxide fuel battery run time at high temperature, the battery does not match the thermal expansion behavior between different components, will cause a larger internal strain gradient, stress is not the same in different places, leading to cell degeneration, layered or broken." Team professor zhou is introduced, due to the excellent REDOX catalytic activity and high electrical conductivity, the fuel cell is one of the most popular cathode materials containing cobalt perovskite oxides, however drill base perovskite cathode of the problem is that their thermal expansion coefficient is very high, is far greater than the commonly used electrolyte, cause thermal mechanical is not compatible.In order to greatly reduce the thermal expansion coefficient of cobalt-based electrode, negative influences and no oxygen reduction reaction, south university professor Shao Zong peace week ghost team Termisk expansionskompensationsstrategi framförs för att övervinna den tekniska flaskhalsen: genom sintring av fast fas, sintring, utlöste borrbasen med hög elektrokemisk aktivitet och termisk expansionskoefficient för perovskit och negativa termiska expansionsmaterial tillsammans med en användbar gränssnittsreaktion mellan de två, och bildade således en god matchning av termiska expansionegenskaper hos kompositelektroduktionen med den elektrolyte) mellan de två och bildade således en god matchning av termiska expansionsföretag för kompositelektroduktionen med den elektrolyte {3 -3 -talet {3 yta)